321 ステンレス鋼ストリップ
ステンレス鋼シートプレートグレードBaogu供給
| タイプ | 学年 | 学年 | 化学成分% | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | 他の | |||
| オーステナイト系 | 201 | SUS201 | ≤0.15 | 16.00～18.00 | 3.50-5.50 | 5.50－7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| 202 | SUS202 | ≤0.15 | 17.00～19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | － | ||
| 301 | 1.431 | ≤0.15 | 16.00～18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | ≤0.07 | 17.00～19.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0.030 | 18.00～20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04～0.10 | 18.00～20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0.20 | 22.00～24.00 | 12.00～15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0.08 | 22.00～24.00 | 12.00～15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0.25 | 24.00～26.00 | 19.00～22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00～26.00 | 19.00～22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 314 | 1.4841 | ≤0.25 | 23.00～26.00 | 19.00～22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0.08 | 16.00～18.50 | 10.00～14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0.030 | 16.00～18.00 | 10.00～14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0.08 | 16.00～18.00 | 10.00～14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)～0.70 | |
| 317 | * | ≤0.08 | 18.00～20.00 | 11.00～15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0.03 | 18.00～20.00 | 11.00～15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0.08 | 17.00～19.00 | 9.00～12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)～0.70 | |
| 321H | * | 0.04～0.10 | 17.00～19.00 | 9.00～12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)～0.70 | |
| 347 | 1.455 | ≤0.08 | 17.00～19.00 | 9.00～12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≧10*C%-1.10 | |
| 347H | 1.494 | 0.04～0.10 | 17.00～19.00 | 9.00～12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≧10*C%-1.10 | |
| xm-19 | ニトロニック50 | ≤0.06 | 20時50分～23時50分 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0.2～0.4 | Nb:0.10-0.30 V:0.10-0.30 | |
| 904L | N08904 | ≤0.02 | 19.0～23.0 | 23.0～28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | ≤1.00 | 0.1 | Cu:1.0-2.0 | |||
| デュプレックス | 2205 | S32205 | ≤0.03 | 22.0～23.0 | 4.5-6.5 | ≤2.00 | ≤0.030 | ≤0.020 | 3.0～3.5 | ≤1.00 | - | 0.14～0.20 | |
| 2507 | S32750 | ≤0.03 | 24.0～26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0～5.0 | ≤0.80 | 0.5 | 0.24～0.32 | ||
| * | S32760 | ≤0.03 | 24.0～26.0 | 6.0-8.0 | ≤1.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | ≤1.00 | 0.5～1.00 | 0.2～0.3 | ||
| 2304 | S32304 | ≤0.03 | 21.5-24.5 | 3.0～5.5 | ≤2.50 | ≤0.040 | ≤0.030 | 0.05～0.6 | ≤1.00 | 0.05～0.6 | 0.05～0.2 | ||
| 329 | 1.446 | ≤0.08 | 23.00～28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | ||
| フェライト | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)～0.50 Nb:0.17 |
| 430 | 1Cr17 | ≤0.12 | 16.00～18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | S44600 | ≤0.20 | 23.00～27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0.25 | - | |
| マルテンサイト | 410 | 1Cr13 | 0.08～0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0.15 | 12.00～14.00 | 3) | ≤1.25 | ≤0.060 | ≥0.15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00～14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26～0.35 | 12.00～14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0.20 | 15.00～17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440℃ | 11Cr17 | 0.95～1.20 | 16.00～18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0.07 | 15:00～17:50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| 631 | 午後17時から午後7時 | ≤0.09 | 16.00～18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | アルミニウム 0.75-1.50 | |
| 632 | 15-5時 | ≤0.09 | 14.00～16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2.5～4.5 | - | アルミニウム 0.75-1.50 | |
説明
321 ステンレス鋼ストリップは、炭素含有量が低く、多くの腐食環境に対して優れた耐食性を備えたオーステナイト系ステンレス鋼の一種です。321 は、優れた溶接性、良好な機械加工性、優れた加工特性を備えています。
321 ステンレス鋼ストリップは、食品および飲料産業だけでなく、化学産業、紙パルプ産業、海洋および海洋エンジニアリング産業でも一般的に使用されています。
321 ステンレス鋼ストリップは、塩化物応力腐食割れや孔食に対する高いレベルの耐性も備えています。また、250°C (480°F) までの高温での塩酸にも耐性があります。
特徴
優れた耐食性: 321 ステンレス鋼ストリップは、304 および 316 タイプのステンレス鋼よりも優れた耐食性を備えているため、腐食環境での使用に最適です。
優れた溶接性：321ステンレス鋼帯は、アーク溶接（TIG/GTAW）、電子ビーム溶接（EBW/EFW）、サブマージアーク溶接（SAW）、レーザービーム溶接（LBIW）を含むあらゆる方法で溶接できます。
高強度: 321 ステンレス鋼ストリップの強度レベルは、炭素含有量とオーステナイト粒径が増加しているため、304 タイプのステンレス鋼よりも最大 50% 高く、316 タイプのステンレス鋼よりも最大 80% 高くなります。